Affiliation:
1. Institute for Plasma Research 1 , Gandhinagar, Gujarat 382016, India
2. Homi Bhabha National Institute, BARC Training School Complex 2 , Anushaktinagar, Mumbai, Maharashtra 400094, India
Abstract
The surface of austenitic stainless steel AISI 304L has been hardened by adding nitrogen and carbon through the plasma nitrocarburizing process. Plasma nitrocarburizing at low temperatures eliminates the formation of nitrides and carbides of chromium, thereby increasing the surface hardness without compromising its corrosion resistance. This is attributed to the presence of a hard case consisting of a solid-solution of nitrogen and carbon occupying interstitial sites in an “expanded” austenite phase. The expanded austenite is further characterized as nitrogen-expanded austenite (γN) and carbon-expanded austenite (γC). In the present work, austenitic stainless steel AISI 304L samples were plasma nitrocarburized by varying the N2 content (%N2) in N2-H2-C2H2 feed gas mixture and treatment times (3, 5, and 7 h) at 673 K and 500 Pa. The samples were characterized by means of XRD, microindentation, XPS, EIS, and potentiodynamic polarization testing, for studying the microstructural, mechanical, and electrochemical properties. The XRD analysis revealed the presence of ɛ'N and γ'N in addition to γN and γC when treated with higher %N2 gas for 5 and 7 h. From XPS, the binding energies of undefined FexN were obtained which were found to lie very close to the defined FexN for higher %N2 gas. Surface hardness significantly improved after the plasma nitrocarburizing processes irrespective of the %N2 and treatment times compared to the untreated AISI 304L. The presence of CrN precipitation on the surface of samples treated with the 75% N2 for 5 and 7 h were observed from XPS, which caused higher corrosion rate. Among the treated samples, the process with 50% N2 and 5 h exhibited the best corrosion resistance with high surface hardness.
Funder
Department of Atomic Energy, Government of India
Subject
Surfaces, Coatings and Films,Surfaces and Interfaces,Condensed Matter Physics
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献