Synthesis and property of polyurethane elastomer for biomedical applications based on nonaromatic isocyanates, polyesters, and ethylene glycol

Abstract

AbstractPolyurethane (PU) elastomers were synthesized by the reaction of HDI or IPDI diisocyanates and poly(ε-caprolactone) (PCL or poly(ethylene adipate) (PA) diols and ethylene glycol as a polymer chain extender. IR, 1H, and 13C NMR spectroscopy and X-ray analysis were used for the structural analysis of the formed films. The molecular weight distribution was examined by GPC chromatography. Based on the measured contact angles, free surface energy parameters were calculated. The obtained results were analyzed for the possible use of these polyurethanes as biomaterials. The most promising in this respect was PU-3, which was synthesized from IPDI and PCL. This was due to its high molecular weight of approximately 90,000, the presence of a crystalline phase, and the relatively high hydrophobicity, with a SEP value below 25 mJ/m2. These films showed a good resistance to hydrolysis during incubation in Baxter physiological saline during 6 weeks. Both Gram-positive (Bacillus sp.) and Gram-negative (Pseudomonas sp.) types of bacterial strains were used to test the biodegradation property. Synthesized PUs are biodegradable and showed moderate or even mild cytotoxicity against human normal fibroblasts (BJ) and immortalized keratinocytes (HaCaT), estimated with direct contact assay. The most biocompatible was PU-3 film, which revealed rather mild reactivity against both cell lines, and the least was PU-2 film, synthesized from HDI and PA (severe toxicity for HaCaTs).