High-density direct laser deposition (DLD) of CM247LC alloy: microstructure, porosity and cracks

Author:

Bidare Prveen,Mehmeti Aldi,Jiménez Amaia,Li Sheng,Garman Chris,Dimov Stefan,Essa Khamis

Abstract

AbstractNickel-based alloys are known as non-weldable materials due to their complex characteristics. Consequently, additive manufacturing of these alloys is particularly challenging. In this paper, the influence of process parameters on the porosity, crack formation and microstructure of additively manufactured CM247LC nickel-based alloy is analysed. The feasibility of the direct laser deposition (DLD) process to manufacture crack-free and low-porosity CM247LC samples is studied. CM247LC samples were built on Inconel 718 that has similar chemical composition, to form hybrid superalloy parts. It was shown that crack-free and high-density CM247LC samples can be obtained through DLD without significant substrate preheating for certain parameter combinations: laser power in the range of 800–1000 W and powder feed rates between 6 and 8 g/min. High-cost and complex preheating was avoided that was commonly reported as necessary to achieve similar densities. For hybrid parts, a large beam diameter and slow scan speeds were employed to achieve optimal conditions as it was evident from the achieved bonding between the Inconel 718 substrate and the deposited layers. It was observed that good bonding between the two materials can be obtained with laser power values between 800 and 1000 W, scanning speed higher than 300 mm/min and powder flow rates of 6–8 g/min.

Funder

MBDA UK Limited

Publisher

Springer Science and Business Media LLC

Subject

Industrial and Manufacturing Engineering,Computer Science Applications,Mechanical Engineering,Software,Control and Systems Engineering

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3