Microstructure and mechanical properties of Zr3Al3C5-based ceramics synthesized by Al-Si melt infiltration

Author:

Fan Xiaomeng,Ma Yuzhao,Deng Yangfang,Ding Jinxue,Cheng Laifei

Abstract

AbstractIn this work, bulk Zr3Al3C5-based ceramics were synthesized by the infiltration of Al-Si melt into zirconium carbide (ZrC) perform. The phase composition, microstructure, and mechanical properties of as-fabricated ceramics were studied. The results demonstrate that Si is more effective to reduce the twin boundary energy of ZrC than Al, and thus promotes the decrease of formation temperature of Zr3Al3C5. With the infiltration temperatures increasing from 1200 to 1500 °C, the Zr3Al3C5 content increases from 10 to 49 vol%, which is contributed to the increase of flexural strength from 62±9 to 222±10 MPa, and fracture toughness (KIC) from 2.8±0.2 to 4.1±0.3 MPa·m1/2. The decrease of mechanical properties for the samples fabricated at 1600 °C is ascribed to the abnormal growth of Zr3Al3C5 grains.

Publisher

Springer Science and Business Media LLC

Subject

Ceramics and Composites,Electronic, Optical and Magnetic Materials

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3