Chen Xiaowu,Cheng Guofeng,Zhang Junmin,Guo Feiyu,Zhou Haijun,Liao Chunjin,Wang Hongda,Zhang Xiangyu,Dong Shaoming
Abstract
AbstractResidual stress originated from thermal expansion mismatch determines the mechanical properties of ceramic matrix composites (CMCs). Here, continuous SiC fiber reinforced SiC matrix (SiCf/SiC) composites were fabricated by nano-infiltration and transient eutectic-phase (NITE) method, and the residual stress of the composites was investigated using high-temperature Raman spectrometer. With temperature increasing from room temperature to 1400 °C, the residual stresses of the matrix and the fiber decrease from 1.29 to 0.62 GPa and from 0.84 to 0.55 GPa in compression respectively, while that of the interphase decreases from 0.16 to 0.10 GPa in tension. The variation of residual stress shows little effect on the tensile strength of the composites, while causes a slight decrease in the tensile strain. The suppression of fiber/matrix debonding and fiber pulling-out caused by the residual stress reduction in the interphase is responsible for the decreasing tensile strain. This work can open up new alternatives for residual stress analysis in CMCs.
Publisher
Springer Science and Business Media LLC
Subject
Ceramics and Composites,Electronic, Optical and Magnetic Materials
Cited by
38 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献