Application of cesium hydroxide monohydrate for ring opening polymerization of monosubstituted oxiranes: characterization of synthesized polyether-diols

Abstract

AbstractCesium hydroxide monohydrate (CsOH·H2O) activated by cation complexing agents, i.e., 18C6 or C222 was applied as initiator of monosubstituted oxiranes polymerization. Propylene oxide (PO), 1,2-butylene oxide (BO), styrene oxide (SO) and some glycidyl ethers were used as monomers. All processes were carried out in tetrahydrofuran solution at room temperature. Such polymers, as PPO-diols, PBO-diols and PSO-diols, are unimodal and have molar masses Mn = 2000–5100. Their dispersities are rather high (Mw/Mn = 1.17–1.33). Moreover, PPO-diols and PSO-diols are not contaminated by monools with unsaturated starting groups. Poly(glycidyl ether)s are, in general, polymodal. For example, poly(isopropyl glycidyl ether)-diols are bi- or trimodal, whereas poly(allyl glycidyl ether)-diols possess two or even six fractions. Molar masses of main fraction are 4200–6400, and the second fraction is much lower, namely 600–2600. Dispersities of some fractions are very low (Mw/Mn = 1.01–1.07). Polymodality of polymers obtained was discussed in terms of the formation of two or more species propagating with different rate constants. Graphic abstract