Photo-Chlorine Production with Hydrothermally Grown and Vacuum-Annealed Nanocrystalline Rutile

Abstract

AbstractPhoto-generated high-energy surface states can help to produce chlorine in aqueous environments. Here, aligned rutile (TiO2) nanocrystal arrays are grown onto fluorine-doped tin oxide (FTO) substrates and activated either by hydrothermal Sr/Ba surface doping and/or by vacuum-annealing. With vacuum-annealing, highly photoactive films are obtained with photocurrents of typically 8 mA cm−2 at 1.0 V vs. SCE in 1 M KCl (LED illumination with λ = 385 nm and approx. 100 mW cm−2). Photoelectrochemical chlorine production is demonstrated at proof-of-concept scale in 4 M NaCl and suggested to be linked mainly to the production of Ti(III) surface species by vacuum-annealing, as detected by post-catalysis XPS, rather than to Sr/Ba doping at the rutile surface. The vacuum-annealing treatment is proposed to beneficially affect (i) bulk semiconductor TiO2 nanocrystal properties and electron harvesting, (ii) surface TiO2 reactivity towards chloride adsorption and oxidation, and (iii) FTO substrate performance.