Effect of Shot Peening on Oxidation and Precipitation in Inconel 718

Abstract

AbstractIn this study, the effect of the surface state on the behaviour of Inconel 718 alloy exposed to 640 $$^{\circ }$$ ∘ C and 700 $$^{\circ }$$ ∘ C environments for times varying between one and one hundred hours was investigated. In particular, the focus was set on the evolution of oxidation and precipitation phenomena during thermal exposure. Three surface states were considered: two generated through shot peening treatments featuring different coverage levels, while the third condition is a non-peened one. Shot peening treatments modify the surface condition and introduce higher residual stresses and microhardness values than in the non-treated condition. The morphology of the oxides appears to be different depending on the condition observed. Regarding the kinetics, over time the oxidation process follows a parabolic trend and appears to be influenced by the surface state; in particular, severe shot peening treatment is characterized by the highest intensity of the phenomenon. However, the order of magnitude of the weight gains measured suggests that the observed variations can be neglected, and that the positive effect of shot peening can be exploited without introducing oxidation problems. From the point of view of the microstructural evolution, an increase in the coarsening kinetics of $$\gamma$$ γ ” phase was observed in the shot peened layer.