Abstract
AbstractThe paper presents the research results on duplex corrosion-resistant chromium–nickel–molybdenum cast steel of the GX2CrNiMoCuN 25-6-3-3 grade. The aim was to determine the effect of the soaking temperature for the hyperquenching process Tp, that is, 950 to 1200 °C, on the microstructure and mechanical properties, that is UTS tensile strength, the yield strength, HB Brinell hardness, the elongation EL and impact strength KV of the steel, cast under industrial conditions with the minimum content of Cr, Ni, Mo and Cu according to the PN-EN 10283 standard. On the basis of the results, it was confirmed that the hyperquenching guarantees the elimination of the brittle intermetallic phase in the steel microstructure. In addition, the most favorable strength-to-ductility ratio of the steel with an almost equal amount of austenite γ and ferrite α in its microstructure was obtained using the soak temperature of 1080 °C, which was considered optimal for the above-mentioned duplex cast steel.
Publisher
Springer Science and Business Media LLC
Subject
Materials Chemistry,Metals and Alloys,Industrial and Manufacturing Engineering,Mechanics of Materials
Reference21 articles.
1. H. Eriksson, S. Bernhardsson, The applicability of duplex stainless steels in sour environments. Corros. Sci. 47(9), 719–725 (1991). https://doi.org/10.5006/1.3585312
2. B. Voronenko, Austenitic-ferritic stainless steels: a state-of-the-art review. Met. Sci. Heat Treat. 39(10), 428–437 (1997)
3. M. Chen, W. Tsai, Stress corrosion cracking behaviour of 2205 duplex stainless steel in concentrated NaCl solution. Corros. Sci. 42(3), 545–559 (2000). https://doi.org/10.1016/S0010-938X(99)00105-5
4. B. Kalandyk, Characteristics of microstructure and properties of castings made from ferritic-austenitic steel. (Archives of foundry engineering, Katowice–Gliwice, Poland, 2011)
5. E. Edwards, D. Hodgkinson, M. Maxfield, Effect of chemistry and heat treatment on the pitting corrosion resistance of three duplex stainless steel alloys. Int. J. Metalcast. 10(1), 118–121 (2016). https://doi.org/10.1007/s40962-015-0013-3
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献