Abstract
AbstractThis study investigates the change of chemical, structural, and mechanical properties of carbon fibre reinforced polymers (CFRP) after one-sided thermal loading. Therefore, CFRP samples (HexPly® 8552/IM7) with varying thickness (4 and 8 mm) are irradiated at different heat fluxes (15, 30, and 50 kW/m2). For a depth-resolved view on matrix degradation inside the CFRP, infrared spectroscopy (ATR-FTIR) is applied along a ground incline plane. A change of structural properties in the form of developing delaminations is investigated with microfocused computed X-ray tomography (µCT). The loss of residual strength is determined by means of interlaminar shear strength testing (ILSS). The evaluation of the data shows that delaminations occur predominantly dependent on temperature and only beyond a certain level of matrix degradation traceable by IR spectroscopy. It is also shown that delaminations are mainly responsible for the loss of strength. Furthermore, linear discriminant analysis (LDA) is performed to predict the presence of delaminations. This information provides a basis for a reliable prediction of the residual strength by IR spectroscopy after one-sided thermal loading.
Publisher
Springer Science and Business Media LLC
Reference46 articles.
1. Schürmann, H.: Konstruieren mit Faser-Kunststoff-Verbunden. 2nd edition, Springer (2007)
2. Tant, M.R., Connel, J.W., McManus, H.L.N.: High-Temperature Properties and Applications of Polymeric Materials. ACS Symposium Series (1995)
3. Mouritz, A.P., Gibson, A.G.: Fire Properties of Polymer Composite Materials, Springer (2006)
4. Henderson, J.B., Wiebelt, J.A., Tant, M.R.: A Model for the Thermal Response of Polymer Composite Materials with Experimental Verification. J. Compos. Mater. 19, 579–595 (1985)
5. Milke, J.A., Vizzini, A.J.: Thermal Response of Fire-Exposed Composites. J. Compos. Tech. Res. 13, 145–151 (1991)
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献