Abstract
AbstractWe present results from a systematic investigation of environmental effects on the frictional behavior of Au–Ni multilayer films of varying interlayer spacing. The current results, sliding against ruby spheres in a dry N2 atmosphere, are compared to prior work on the tribological behavior of these materials under ultra-high vacuum (UHV) (Cihan et al. in Sci Rep 9:1–10, 2019). Under both conditions, there is a regime of high friction when the interlayer spacing is large and a regime of low friction when the spacing is small. The low friction regime is associated with a critical grain size below which grain boundary sliding is expected to be the dominant mechanism of deformation. A shear-induced alloy formation (60–65 at.% Ni in Au) and a concomitant low friction coefficient was observed with multilayer spacings of 20 nm and lower under UHV. A distinct microstructure was found in dry N2, and is attributed to different interfacial characteristics due to adsorbed species; rather than mixing between Au and Ni layers, only the uppermost Au layers were affected by shearing. These observations are coupled with the friction and wear behavior of multilayer samples sliding under different environments.
Funder
Deutsche Forschungsgemeinschaft
Publisher
Springer Science and Business Media LLC
Subject
Surfaces, Coatings and Films,Surfaces and Interfaces,Mechanical Engineering,Mechanics of Materials
Reference32 articles.
1. Roberts, E.W.: Space tribology: its role in spacecraft mechanisms. J. Phys. D 45, 503001 (2012)
2. Gola, A.: Deformation of metallic multilayers: an atomistic study of the relationship between structure and deformation mechanisms. Karlsruhe (2019)
3. Godet, M.: The third body approach: a mechanical view of wear. Wear 100, 437–452 (1984)
4. Bowden, F.P., Tabor, D.: Mechanism of metallic friction. Nature 150, 197–199 (1942)
5. Lancaster, J.K.: A review of the influence of environmental humidity and water on friction, lubrication and wear. Tribol. Int. 23(6), 371–389 (1990)
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献