AbstractIn this work, three samples of bauxite were used as inexpensive sources for the zeolite formation by a green process based on vapor-phase crystallization (VPC) method. The synthesis was carried out using a water bath with deionized water heated at 35, 45, 60 or 90 °C. During the process, NaOH pre-fused bauxites were contacted only with vapor from the liquid. The results indicate that sodalite formed in all the samples after VPC at higher temperatures (60 °C and 90 °C). Large amount of zeolite A was instead synthesized in the sample characterized by SiO2/Al2O3 ratio next to 1 and after vapor treatment at 35 °C and 45 °C. These data highlight the determining role of both raw material chemical composition and amount of water molecules in type of zeolite formed by vapor crystallization method. Moreover, the results indicate that VPC process made it possible to synthesize zeolite generating no water waste.
Publisher
Springer Science and Business Media LLC
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference56 articles.
1. Agosta F, Manniello C, Cavalcante F, Belviso C, Prosser G (2021) Late cretaceous transtensional faulting of the Apulian platform. Italy Mar Pet Geol 127:104889
2. Bardossy´ G, Boni M, Dall’Aglio M, D’Argenio B, Panto G (1977) Bauxites of peninsular Italy: composition, origin and geotectonic significance. Gebr Borntraeger 15:
3. Gu J, Huang Z, Fan H, Jin Z, Yan Z, Zhang J (2013) Mineralogy, geochemistry, and genesis of the lateric bauxite deposits in the Wuchuan-Zheng’an-Daozhen area, Northern Guizhou Province, China. J Geochem Explor 130:44–59
4. Choi YS, Lee MS, Oh SH (2002) Manufacturing method of zeolite 4A using bauxite. KR Patent 094527-A; 415941-B
5. Choi YS, Lee MS, Oh SH (2004) Method for preparing zeolite. KR Patent 028246-A; 491091-B
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献