High-Performance Polyamide/Carbon Fiber Composites for Fused Filament Fabrication: Mechanical and Functional Performances

Abstract

AbstractThis study is focused on the 3D printing by fused filament fabrication (FFF) process of short carbon-fiber-reinforced polyamide (PA) composites. In particular, the effect of short carbon fiber (CF) on the mechanical, electrical and piezoresistivity properties of 3D-printed polyamide (PA) composite parts has been analyzed. In comparison with neat PA, the results revealed that the carbon fibers effectively improved all assessed mechanical properties of PA/CF composites. In particular, in XY build orientation, PA/CF 3D-printed composites exhibited a tensile strength of 96 MPa and a tensile modulus of 7.9 GPa, with an increment of + 34 and + 147%, respectively, when compared to the neat PA. Interlayer strength of 3D-printed PA and PA/CF composites reaches similar values, in the range 26-28 MPa. The impact strength of 3D-printed XY parts was reduced by the presence of CF. However, the fracture toughness of PA/CF composite 3D-printed parts was slightly higher in comparison with that of neat PA. Electrical resistivity of PA/CF 3D-printed parts is gradually decreasing from 1.7 × 104 to 0.7 × 104 Ω cm in the temperature range from − 16 to 100 °C. The piezoresistivity tests revealed that an exponential resistance change occurs for both compression-molded and 3D-printed PA/CF samples once strained in tension. A gauge factor of 3D-printed parts of about 65 ± 5 was determined from cyclic strains in the elastic region.