Defect-Correlated Vickers Microhardness of Al-Si-Mg Alloy Manufactured by Laser Powder Bed Fusion with Post-process Heat Treatments

Abstract

AbstractLaser powder bed fusion is an additive manufacturing process characterized by different advantages like the manufacture of samples with complex geometry without the use of tools and/or molds. Generally, the manufactured samples are characterized by high tensile strengths which, however, can be affected by the presence of defects due to the unoptimized process parameters. In a large applications field, a low density of the as-built AlSi10Mg samples is a very important parameter to considered, e.g., due to both the loss of the tensile strengths correlated with a premature failure of the samples and the increase in time and costs associated with the manufacturing process. In addition, different post-process heat treatments can increase these effects leading to an ineffective manufacturing process. In this scenario, the present work shows the analysis of spherical and lack-of-fusion pores induced by the laser powder bed fusion process on the AlSi10Mg samples and their variations after different heat treatments (direct aging and T6). At the same time, the influence of pores on the Vickers microhardness and the tensile properties has been studied in the same AlSi10Mg samples (bars and billets) that were printed with single- and double-laser machine setup. Different process parameters were also analyzed and compared. The study was supported by the microstructural and pore analysis performed by optical microscopy along the XZ plane (build direction) and the XY plane. Finally, the greatest effects of pores were observed on the Vickers microhardness values; in fact, two different relationships between microhardness and density variation are discussed. The T6 heat treatment leads to a rounding of the pores already formed in the as-built samples and to a formation of new small pores. Graphical Abstract