Kymäläinen Maija,Dömény Jakub,Schwarzkopf Matthew,Šeda Vit,Rautkari Lauri
Abstract
AbstractSurface carbonization, or charring, of wooden exterior cladding boards is a modification method that creates a fully organic barrier layer in resemblance to a coating. The process effectively degrades the wood and transforms it into a carbonaceous residue that protects the underlying unmodified wood from environmental stresses. The surface quality of wood modified in this manner is a combination of several factors and depends on the manufacturing method and wood species. To assess the quality of spruce and birch modified with contact and flame charring techniques, several experiments were set up from the nanoscale to macroscopic evaluation of surface resistance to different stresses. The changes in elemental composition are scaled with the modification severity with little differences between wood species. The carbon structures analyzed by high-resolution transmission electron microscopy (HR-TEM) were found to be amorphous, but the electron energy-loss spectroscopy (EELS) revealed higher ordering with what is assumed to be random graphitic stacking of carbon sheets. These carbon–carbon bonds are stable, so a higher ordering is hypothesized to induce improved resistance to exterior stresses. The scanning electron microscopy (SEM) revealed a clear difference between contact-charred and flame-charred woods. The selected contact charring temperature was not high enough to induce the transformation of cell walls from anisotropic into an isotropic material but provided other benefits such as a relatively crack-free, smooth and scratch resistant surface. Surface roughness was able to adequately predict the surface quality of the contact-charred samples, and scratch tests were found to be suitable for evaluating the mechanical stress resistance of the surface instead of abrasion. In terms of overall quality, birch instead of spruce was concluded to better respond to both charring methods, although contact charring eliminates some species-specific characteristics, resulting in more homogeneous surfaces.
Publisher
Springer Science and Business Media LLC
Subject
Industrial and Manufacturing Engineering,Plant Science,General Materials Science,Forestry
Reference55 articles.
1. Allen NS, Pena JM, Edge M, Liauw CM (2000) Behaviour of carbon pigments as excited state quenchers in LDPE. Polym Deg Stabil 67(3):563–566
2. Anca-Couce A, Obernberger I (2016) Application of a detailed biomass pyrolysis kinetic scheme to hardwood and softwood torrefaction. Fuel 167:158–167. https://doi.org/10.1016/j.fuel.2015.11.062
3. Andreae MO, Gelencsér A (2006) Black carbon or brown carbon? The nature of light-absorbing carbonaceous aerosols. Atmos Chem Phys Discuss 6:3419–3463
4. Antal MJ, Grønli M (2003) The art, science, and technology of charcoal production. Ind Eng Chem Res 42:1619–1640
5. Aytin A, Korkut S, As N, Ünsal Ö, Günduz G (2015) Effect of heat treatment of wild cherry wood on abrasion resistance and withdrawal capacity of screws. Drvna Ind 66(4):297–303