Abstract
AbstractHot dip galvanizing is a surface treatment used to form a corrosion-resistant layer on the surface of steel by dipping it in a liquid zinc bath. However, a lot of structures used for hanging or containing the parts during the process are made of steel and suffer from liquid zinc corrosion. Furthermore, Fe–Zn intermetallics formed on the surface induce an additional pickling and zinc consummation, therefore generating supplementary economic and environmental costs. In this article, two Fe-Cr-Ni-Si coatings synthetized by the slurry process on carbon steel (C22) were characterized by XRD, EDX, EPMA and EBSD analyses. Their corrosion protective properties were studied in the process imitating cyclic batch galvanizing and compared to those of uncoated carbon steel (C22) and stainless steel (316 L). The coatings were verified to be more efficient than the 316 L steel usually used for this application. After 9 cycles of no weight loss, molten zinc corrosion was linear and the same for Fe-Cr-Ni-Si coatings as for the stainless steel.
Funder
Université de Lille
Conseil Régional Hauts-de-France
Publisher
Springer Science and Business Media LLC
Subject
General Earth and Planetary Sciences,General Physics and Astronomy,General Engineering,General Environmental Science,General Materials Science,General Chemical Engineering
Reference29 articles.
1. Kergar Neghab A, Hrymak AN, Goodwin FE (2015) In: 10th International Conference on Zinc and Zinc Alloy Coated Steel Sheet (Galvatech 2015), AIST, Toronto, Canada
2. Zhang K, Tang NY, Goodwin F (2007) Reaction of 316L stainless steel with a galvanizing bath. J of Mater Sci 42:9736–9745. https://doi.org/10.1007/s10853-007-1978-y
3. Hardy Y, Dubois M, Bertrandie JJ, Saint-Raymond H (2007) In: 7th International Conference on Zinc and Zinc Alloy Coated Steel Sheel (Galvatech ‘07), Osaka, Japon
4. Perrot P, Tissier JC, Dauphin JY (1992) Stable and metastable equilibria in the Fe–Zn–A1 system at 450°C. Z. für Metallkunde. 83(11):786–790. https://doi.org/10.1515/ijmr-1992-831104
5. Yamaguchi S, Makino H, Sakatoku A, Iguchi Y (1995) In: International Conference on Zinc and Zinc Alloy Coated Sheet Steel (Galvatech ‘95), Chicago, IL
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献