AbstractMaraging steels are a class of low-carbon ultra-high-strength martensitic steels. Due to their excellent weldability, these steels have been widely applied for laser-based additive manufacturing (AM). MAR-60HRC is a newly developed maraging grade for AM with a nominal chemical composition of 13.0Ni-15.0Co-10.0Mo-0.2Ti, Fe bal. (wt%), capable of achieving hardness levels of ~ 740 HV. Alternatively, 18Ni300 is a commercialized maraging steel with an excellent combination of strength and toughness at the peak aged hardness (i.e., ~ 590 HV). This work aims to investigate the properties and microstructure of MAR-60HRC fabricated by Laser Directed Energy Deposition (L-DED). Further, the manufacturability of bimetallic parts comprising a tough 18Ni300 core and a hard MAR-60HRC on the surface was evaluated. After proper aging, the multi-layered material showed a surface hardness of ~ 720 HV1 and apparent fracture toughness of 71 MPa m1/2, higher than that of MAR-60HRC (i.e., 60 MPa m1/2), and lower than 18Ni300 (i.e., 90 MPa m1/2). The excellent combination of surface hardness and fracture toughness was discussed, considering the crack arrest at the interface and the flawless interface between the two steels.
Graphical Abstract
Funder
Ministero dell’Istruzione, dell’Università e della Ricerca
Università degli Studi di Trento
Publisher
Springer Science and Business Media LLC
Subject
Materials Chemistry,Metals and Alloys,Mechanics of Materials,Condensed Matter Physics