Experimental Investigation on Bonded and Screwed Carbon Fiber-Reinforced Plastic Plates on Timber Column–Sill Joints

Author:

Ueda Rintaro,Sakamoto Akio,Sawata KeiORCID,Sasaki Yoshihisa,Sasaki Takanobu

Abstract

AbstractIn this study, timber column–sill joints strengthened with carbon fiber-reinforced plastic (CFRP) plates using bonds and screws were subjected to loading tests. Twelve joint specifications were considered depending on different combinations of the CFRP plate surface finish and thickness and the type of bond, and the corresponding effects on the load–displacement behavior of the joints were investigated. Three failure modes were observed in addition to the peeling of the CFRP plate. The specimens that failed owing to screw tear out and screw head pull-through in the CFRP plate or splitting of the sill showed load–displacement curves of a similar shape. Those that failed owing to buckling of the CFRP plate showed a rapid and substantial load decrease due to failure. This failure mode was only observed in 0.50 mm thick CFRP plate specimens. When a peel-ply CFRP plate was installed in the column–sill joint specimens, similar secant stiffnesses were observed in the silicon and epoxy resin-bonded specimens, both with high shear strength. Although the specimens with bonds with a high shear strength showed lower deformation performance, the specimens' maximum load increased with the bond's shear strength. The maximum load improved for a 0.75 mm thick peel-ply silicon- or epoxy-bonded CFRP plate. The load's maximum value after peeling the CFRP plate was 0.79–1.23 times as large as the maximum load of the no-bond specimens and did not change significantly.

Funder

Tokyo Metropolitan Small and Medium Enterprise Support Center

Publisher

Springer Science and Business Media LLC

Subject

Civil and Structural Engineering,Geotechnical Engineering and Engineering Geology

Reference28 articles.

1. Japan Building Disaster Prevention Association (2011) Revision for 2010 Guide for design and construction of aseismic retrofitting of existing reinforced concrete construction utilizing continuous carbon fiber reinforcement material (in Japanese)

2. American Concrete Institute (2008) Guide for design and construction of externally bonded frp systems for strengthening concrete structures

3. Consiglio Nazionale delle Ricerche (2006) Guide for the design and construction of externally bonded FRP systems for strengthening existing structures

4. Cao S, Chen J, Pan J, Sun N (2007) ESPI measurement of bond–slip relationships of FRP–concrete interface. J Compos Constr 11(2):149–160

5. Mazzotti C, Savoia M, Ferracuti B (2008) An experimental study on delamination of FRP plates bonded to concrete. Constr Build Mater 22(7):1409–1421

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3