Fracture toughness of alloy 690 and EN52 welds in air and water

Published:2002-06 Issue:6 Volume:33 Page:1725-1735
ISSN:1073-5623
Container-title:Metallurgical and Materials Transactions A
language:en
Short-container-title:Metall and Mat Trans A

Author:

Brown C. M.,Mills W. J.

Publisher

Springer Science and Business Media LLC

Subject

Metals and Alloys,Mechanics of Materials,Condensed Matter Physics

Link

http://link.springer.com/content/pdf/10.1007/s11661-002-0181-7.pdf

Reference21 articles.

1. C.M. Brown and W.J. Mills: Corrosion, 1999, vol. 55, pp. 173–86.

2. K. Norring, J. Engstrom, and P. Norberg: Proc. 3rd Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, TMS, Warrendale, PA, 1988, pp. 587–93.

3. EPRI Report;R.G. Aspden,1990

4. R.A. Page: Corrosion, 1983, vol. 39, pp. 409–21.

5. T. Yonezawa, K. Onimura, N. Sasaguri, T. Kusakabe, H. Nagano, K. Yamanaka, T. Minami, and M. Inoue: Proc. 2nd Int. Symp. on Environmental Degradation of Materials in Nuclear Power Systems—Water Reactors, ANS, La Grange Park, IL, 1986, pp. 593–600.

Cited by 12 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. Hydrogen contribution to low temperature embrittlement during PWR exposure of an alloy 82 weld metal;International Journal of Hydrogen Energy;2024-04

2. Studies on Long-term Stress Corrosion Cracking Resistance for TT Alloy 690;Materia Japan;2020-12-01

3. Hydrogen-induced brittle fracture in nickel based alloy 82 weld metal;Corrosion Science;2019-06

4. A Mechanistic Study of Stress Corrosion Crack Propagation in Heavily Cold Worked TT Alloy 690 Exposed to Simulated PWR Primary Water;The Minerals, Metals & Materials Series;2017-10-07

5. Methodology for Estimating Thermal and Neutron Embrittlement of Austenitic Stainless Steel Welds During Service in Light Water Reactors;Journal of Pressure Vessel Technology;2016-04-28