Planar-Biaxial Thermo-mechanical Fatigue Behavior of Nickel-Base Superalloy Inconel 718 Under Proportional Loading

Abstract

AbstractThe planar-biaxial thermo-mechanical fatigue behavior of nickel-base superalloy Inconel 718 was studied for selected proportional loading conditions, in particular biaxial strain ratios of 1.0, 0.6, and − 1.0. The cyclic temperature loading with minimum and maximum temperatures of 400 °C and 630 °C and a duration of 250 seconds was either In-Phase or Out-of-Phase to the mechanical axes. Besides the multiaxial tests, uniaxial thermo-mechanical fatigue tests were conducted In-Phase and Out-of-Phase with the same temperature cycle and cycle duration. The performed thermo-mechanical fatigue tests were analyzed regarding the deformation and lifetime behavior and compared with high-temperature isothermal low-cycle fatigue tests from a previous work of the authors. On the side of the lifetime description, a strain- and a stress-based approach were presented. For the planar-biaxial tests, the crack initiation mechanism and crack paths were shown.