Abstract
Abstract
The optical appearance of electroplated chromium layers is a crucial factor for decorative applications. Currently in the decorative chromium plating industry the so far used hexavalent electrolytes are being replaced progressively by solutions of trivalent chromium. However, chromium deposited from trivalent baths tends to have a yellowish color hue at thicknesses beyond 100 nm, which is undesired for most applications. The shift in color is related to a change in surface morphology due to the globular growth of the chromium nuclei. By utilizing pulsed current with on-times in the range of seconds, the grain growth is suppressed and the formation of fresh nuclei is favored. As a result, the average grain size of the layer can be decreased significantly. Compact chromium layers with small grains and improved color values are formed. A blueish appearance and high brightness were maintained up to thicknesses of more than 200 nm. Based on the results a combination of constant and pulsed current is suggested, yielding similar visual appearance as in the case of pulsed current only, but reaching the targeted film thickness much faster.
Graphic abstract
Publisher
Springer Science and Business Media LLC
Subject
Materials Chemistry,Electrochemistry,General Chemical Engineering
Reference30 articles.
1. Lindsay JH (1997) Decorative and hard chromium plating. Plat Surf Finish 84(8):50–51
2. Snyder DL (2012) Decorative chromium plating basics. Met Finish 110(2):14–21
3. Handy SL, Oduoza CF, Pearson T (2006) Theoretical aspects of electrodeposition of decorative chromium from trivalent electrolytes and corrosion rate study of different nickel/chromium coatings. Trans IMF 84(6):300–308. https://doi.org/10.1179/174591906x162946
4. European Chemicals Agency Authorisation List, EC No. 215–607–8, 231–801–5, 231–889–5, 231–906–6, 232–140–5, 232–143–1, 234–190–3, 236–881–5
5. Gupta VK, Shrivastava AK, Jain N (2001) Biosorption of chromium(VI) from aqueous solutions by green algae Spirogyra species. Water Res 35(17):4079–4085. https://doi.org/10.1016/S0043-1354(01)00138-5
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献