FABRICATION AND ELECTRICAL PROPERTIES OF Au/PVDF-TrFE/LaZrOx/Si(100) STRUCTURE

Abstract

Metal-ferroelectric-insulator-semiconductor structure capacitors with a polyvinylidene fluoride trifluoroethylene (75/25) (PVDF-TrFE) ferroelectric and a lanthanum zirconium oxide ( LaZrO x) insulator layers were fabricated on a p-type Si(100) substrate in this work. The thin films were prepared using the spin-coating method. The LaZrO x thin films were crystallized at 750°C for 30 min in an O 2 ambient. Negligible hysteresis was observed from the C–V (capacitance-voltage) characteristic of the LaZrO x/ Si structure. The equivalent oxide thickness (EOT) was about 8.2 nm. Then the PVDF-TrFE film was spin-coated on the LaZrO x/ Si structure. To crystallize the PVDF-TrFE, the structure was annealed at 165°C for 30 min. The memory window width in the C–V curve of the Au/PVDF - TrFE/LaZrO x/ Si structure was about 4 V for a voltage sweep of ±5 V, and the leakage current density was about 10-8 A/cm 2 at 35 kV/cm for a 100-nm-thick film.