Abstract
The aim of this research was to optimize the mechanically activated synthesis (MAS) technology of the Cr3C2-Ni powder intended for thermal spraying. The MAS production route included ball milling for 72 h (ball-to-powder ratio 20:1) and sintering under 1075 °C in vacuum for 4 h. Sintered compact was crushed, classified by sieving to obtain the fraction suitable for thermal spraying (20–45 μm). The morphology and the phase composition of the powder were analyzed by a scanning electron microscope (SEM) and X-ray diffraction (XRD). The optimal Cr:C ratio found was 7:1. The powder had an equiaxial or a slightly elongated lamellar shape, Cr3C2 carbides in a single powder particle had an elongated shape. The principal phases in the optimized powder were Cr3C2, Cr7C3 and Ni (Cr) solid solution. Coatings from the manufactured powder were produced by the high velocity oxy-fuel (HVOF) spraying. The abrasive wear tests were carried out according to standard ASTM G65. The wear tests showed that the sprayed coatings from the experimental powder exhibited about five times higher wear rate at abrasive wear conditions than the coatings from the reference commercial powder.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference15 articles.
1. H. Sarjas, P. Kulu, K. Juhani, P. Vuoristo, Novel WC-Co spray powders and HVOF sprayed coatings on their bases, Proc. 28th Int. Conf. on Surface Modification Technologies (SMT28), Tampere, Finland, 16th–18th of June 2014, 35–42.
2. Europeans Chemical Agency, Functional Chrome Plating: analysis of alternatives, Non-confidential report, Lanexx Deutschland GmbH (2015) 98.
3. H. Sarjas, P. Kulu, K. Juhani, M. Viljus, V. Matikainen, P. Vuoristo, Wear resistance of HVOF sprayed coatings from mechanically activated thermally synthesized Cr3C2–Ni spray powder, P. Est. Acad. Sci. 65 (2016) 101–106.
4. M.M.M. Sarcar, K. Suman, S. Kamaluddin, Tribological and corrosion behavior of HVOF sprayed WC-Co, NiCrBSi and Cr3C2-NiCr coatings and analysis using design of experiments, Mater. Today: Proc. 2 (2015) 2654–2665.
5. M.A. Aavareh, A. Sarhan, B.B. Razak, W.J. Basirun, The tribological and electrochemical behavior of HVOF-sprayed Cr3C2–NiCr ceramic coating on carbon steel, Ceram. Int. 41 (2015) 5387–5396.
Cited by
5 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献