Abstract
The detailed investigation of internal friction and relative dynamic modulus has been carried out for the γ-MnFe alloys with 61.4at%~86.4at%Mn in the temperature range from -50 to 250 using LMR by means of force vibration method. The internal friction was found to exhibit in turn three peaks from higher temperature to the lower temperature on the internal friction-temperature curves. They are PA,PM and PT progressively. It can be concluded that PA may be connected with the stress-induced motion of magnetic domain. The PM was suggested to be originated from the stress-induced movement of interfaces between the fcc and fct phases. The PT is due to a relaxation process associated with the movement of the {101}-twin boundaries in the fct phase or fcc antiferromagnetic phase.
Publisher
Trans Tech Publications, Ltd.
Reference9 articles.
1. S. C. Chen, C. Y. Chang, C. L. Yan, T. Y. Hsu (Xu Z Y). Materials science and engineering, A264: 262-268 (1999).
2. Y. N. Wang, J. Z. Zhu, Acta Physica Sinica, 15, 341-345 (1959).
3. H. M. Deng, Z. Y. Zhong, Journal of shanghai Jaotong university, 36(1), 28-31 (2002).
4. J. F. Delorme and P. F. Gobin, Metaux 573, 185 (1973);
5. Metaux 574, 209 (1973).
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献