Abstract
The effect of enhanced solution treatment on microstructures, tensile properties, intergranular corrosion and exfoliation corrosion of a 6013 type aluminum alloy proceeded via various solution treatment were investigated by optical microscopy (OM), scanning electron microscopy (SEM), tension testing and corrosion resistance testing. The results show that compared with the conventional solution treatment (560°C×2 h), the enhanced solution treatment (560°C×2 h+570°C×2 h) can improve ultimate tensile strength and elongation, the corrosion resistance become worse after 151°C×8 h+191°C×8 h artificial aging. The tensile strength increase is believed to resulting from the coarse second phases dissolve. The corrosion resistance decrease is due to grain growth.
Publisher
Trans Tech Publications, Ltd.
Reference11 articles.
1. R. Braun. Investigations on the long-term stability of 6013-T6 sheet. Materials Characterization. 2006(56): 85-95.
2. R. Braun, G. Roth. Laser Beam Welded T-Joints of 6013 Aluminium Alloy Sheet. Materials Forum. 2004(28): 832-837.
3. J. Chaudhuri, Y. M. Tan, K. Patni, et al. Comparison of Corrosion-Fatigue Properties of 6013 Bare, Alclad 2024, and 2024 Bare Aluminum Alloy Sheet Materials. JMEPEG. 1992(1): 91-96.
4. S. S. Park, H. Garmestani, G. T. Bae, et al. Constitutive analysis on the superplastic deformation of warm-rolled 6013 Al alloy. Materials Science and Engineering A. 2006: 687-692.
5. F. B. Zhang, X. J. Xu, G. C. Wu, et al. Intergranular resistance of a zirconium microalloyed 6013 type aluminum alloy. Journal of Aeronautical Materials. 2011, 31(1): 52-55.
Cited by
3 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献