SEM<i> In Situ</i> Study on Fatigue Crack Growth of LC9 Aluminum Alloy Subjected to Elevated Temperature-Reference-Cited by-同舟云学术

SEM In Situ Study on Fatigue Crack Growth of LC9 Aluminum Alloy Subjected to Elevated Temperature

Published:2013-10 Issue: Volume:834-836 Page:356-359
ISSN:1662-8985
Container-title:Advanced Materials Research
language:
Short-container-title:AMR

Author:

Cai Zeng Jie¹,Li Xu Dong¹,Jia Ming Ming¹

Affiliation:

1. Naval Aeronautical Engineering Academy Qingdao Campus

Abstract

Experimental investigations of fatigue cracking behavior of LC9 aluminum alloy (AA LC9) subjected to elevated temperature were conducted with scanning electron microscope (SEM). Results indicate elevated temperature is important for the fatigue crack growth of AA LC9. Based on small crack growth, crack growth rate for AA LC9 is characterized.

Publisher

Trans Tech Publications, Ltd.

Subject

General Engineering

Link

https://www.scientific.net/AMR.834-836.356.pdf

Reference8 articles.

1. Biallas G, Maier H J. in-situ fatigue in an environmental scanning electron microscope- potential and current limitations. Int J Fatigue. 29 (2007) 1413-1425.

2. Li Xu-Dong, Wang Xi-Shu, Ren Huai-Hui, Chen Yin-Long, Mu Zhi-Tao. Effect of prior corrosion state on the fatigue small cracking behaviour of 6151-T6 aluminum alloy. Corros. Sci. 55(2) (2012) 26-33.

3. Wang X S, Li Y, Meng X K. An estimation method on failure stress of micro thickness Cu film-substrate structure. Sci China Ser E-Tech Sci. 52 (2009) 2210-2215.

4. Xi-Shu Wang, Xu-Dong Li, Huai-Hui Ren, Hai-Yan Zhao , Ryosuke Murai, SEM in-situ study on high cyclic fatigue of SnPb-solder joint in the electronic packaging. Microelectronics Reliability. 51(2011) 1377-1384.

5. Wang X S, Yan C K, Li Y, et al. SEM in-situ study on failure of nanocrystal metallic thin films and substrate under three point bending. Int J Facture. 15 (2008) 269-279.

Cited by 3 articles. 订阅此论文施引文献订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献

1. A Novel Modified Paris’ Law Based Evaluation of Fatigue Crack Propagation of LD2 under Combination of Corrosion and Cyclic Loadings;Advanced Materials Research;2015-04

2. Fracture Analysis of 6A02 Aluminum Alloy Subjected to Corrosion Fatigue Damage;Advanced Materials Research;2014-07

3. The Research on the Reliability of Helicopter Life Based on Analysis of the Data of Flight Data Recorder;Lecture Notes in Electrical Engineering;2014