Affiliation:
1. Chungnam National University
Abstract
Mechanical properties of 3-ply Cu-Ni-Zn/Cu-Cr/Cu-Ni-Zn clad composite plates prepared by explosive bonding and cold-rolling. No intermetallic compounds were observed at the Cu-Ni-Zn/Cu-Cr interface after explosive bonding and cold-rolling and heat-treatment at 723K. The strength of as-rolled clad plate reached up to 575MPa with the ductility of 30% after heat treatment at 723K for 1 hour. The strength dropped to 510MPa and the ductility increased to 48% after heat treatment at 723K for 1.5 hour. There are no stepwise drops of the flow stress before final fracture, meaning three plates were bonded together until the last moment of the stress-strain curve. The observation of the fractured specimens revealed no interface separation even after fracture. The excellent mechanical reliability and the good interfacial bonding strength can be attributed to the absence of detrimental interfacial reaction compounds between Cu-Ni-Zn and Cu-Cr after annealing.
Publisher
Trans Tech Publications, Ltd.
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献