A considerable test was made to figure out the effects of temperature and sliding conditions on the wear properties of the translucent Dy--Sialon. The friction coefficient was 0.54 at RT, 0.26 at 100 oC, and 0.81 at 600 oC respectively under an applied load of 5N. The wear rate was 6.91×10-15 at RT and 1.0×10-15 at 100 oC for the same Dy--Sialon sample. Obviously Dy-Sialon shows an excellent wear resistance under a suitable sliding condition, a load of 5N and at 100 oC. This appears attractive and important for Dy-Sialon ceramics to be used as a type of special wear resistant materials, with an optical translucence.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference6 articles.
1. J. Takadoum, H. Houmid-Bennani, and D. Mairey: J. Eur. Ceram. Soc., Vol. 18(1998), p.553.
2. D. -F. Wang and Z. -Y. Mao: J. Am. Ceram. Soc., Vol. 78(1995), p.2705.
3. E. Zanoria, S. Danyluk, and M. MvNallan, Tribology Transaction, Vol. 3(1995), p.721.
4. Z. -H. Xie, M. Hoffman, R. J. Moon, P. R. Munroe, and Y. -B. Cheng, Wear, Vol. 280-283(2005), p.1253.
5. M. I. Jones and K. Hirao, J. Mater. Research, Vol. 19(2004), p.2750.