Wetting and Interfacial Behavior of Molten Al on Mo-Ni(Co)-Si Coated SiC Ceramic

Abstract

The Mo-Ni (Co)-Si metallizing coatings on the SiC ceramic substrate were prepared by vacuum cladding process. The wetting and spreading of molten Al on coated SiC ceramic substrates at 900 oC were investigated by the sessile drop technique, and the interfacial behavior of the Al/coated SiC wetting couples was analyzed. The experimental results showed that the final contact angle of Al/M20NiSi coated SiC was close to 0o. With the increase of Mo content in the Mo-Ni-Si coating, the shape of the sessile drop became very irregular due to the strong interactions between the Al drop and the coating, so it was unable to precisely characterize the contact angles of Al/Mo30NiSi and Al/Mo40NiSi systems. The final contact angle of Al/Mo10CoSi coated SiC system was also close to 0o, however, the final contact angle of Al/Mo20CoSi coated SiC system climbed to ~42o with the Mo content increasing from 10 at.% to 20 at.%. The significant increase of contact angle may be caused by the accumulation of Mo near the triple line which can impede the spreading of Al drop.