Abstract
We had done the two-pass grind-hardening experiment on 40Cr steel using the conventional aluminum grinding wheel on a surface grinder, compared the structure and performance of the hardened layer of one-pass grinding with those of two-pass grinding and analyzed the forming mechanism of two-pass grinding hardened layers. The results show that there are a similar martensite structure and change rules of hardened layer of one-pass grinding and two-pass grinding in spite of the different of initial structures, for martensite has tempered by the action of the creep feed grinding temperature field. The depths of hardened layer, microhardness and wear resistance have further improved, but the maximal compressive residual stress and its influencing depth of hardened layer have decreased. The forming mechanism of the two-pass grinding hardened layer is the same as that of the grinding hardened layer of quenched steel.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference5 articles.
1. Brinksmeier E and Brockhoff T: Annals of the CIRP, Vol. 45 (1996) No. 1, pp.283-286.
2. Brinksmeier E and Brockhoff T: HTM, Vol. 49 (1994) No. 5, pp.327-330.
3. Brockhoff T: Annals of the CRIP, Vol. 48 (1999) No. 1, pp.255-260.
4. Zarudi I and L.C. Zhang: Journal of Materials Science, Vol. 37 (2002) No. 18, pp.3935-3943.
5. J.D. Liu, G.C. Wang and K.M. Chen: China Mechanical Engineering. Vol. 15 (2004) No. 17, pp.1573-1576. (Chinese).
Cited by
20 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献