Abstract. This paper investigated the Cf/SiC ceramic matrix composites. By utilizing different interfacial treatment processes to prepare carbon-fiber preform, the preform was then densified by infiltration and pyrolysis(PIP) with polycarbosilan/xylene solution as precursor, and the Cf/SiC ceramic matrix composite specimens were fabricated. Mechanical tests such as bending test and fracture toughness were performed for Cf/SiC samples. The results show that the interfacial bonding strength in the sample with high-temperature treatment process was improved due to removing surface sizing. The samples which were treated up to 1400°C exhibited the highest three-point flexural strength, up to 595MPa; The samples which were treated up to 1400°C and deposited by pyrolytic carbon(PyC) coating shows the highest fracture toughness value which was 20.70MPa•m1/2.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,General Materials Science
Reference10 articles.
1. I.L. Jessen; V.A. Greenhut, Effect of microstructure on the mechanical behavior of continuous -fiber- reinforced ceramic-matrix composites. J. Am. Ceram. Soc. 82(1999) 2753-2761.
2. L.T. Zhang, L.F. Cheng, Y.D. Xu, et al. Discussion on strategies of sustainable development of continuous f iber reinforced ceramic matrix composites. Acta Mater. Compo. Sinica, 24 (2007) 1-6.
3. Y. Ma, Q.S. Ma, C.H. Chen, Overseas research progress in the application of continuous fiber reinforced ceramic matrix composites. Material Letter, 21 (2001) 401-404.
4. B.Z. Jang, L.R. Hwang, J.W. Fergus, et al. Interface compatibility in ceramic-matrix omposites. Composites Science and Technology, 56 (1996) 1341 - 1350.
5. D.W. Richerson, Ceramic Components in Gas Turbine Engines: Why Has It Taken So Long?, Ceram. Eng. Sci. Proc., 25 (2004).
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献