Abstract
Texture evolution during static primary recrystallization of an austenitic Fe-28Mn-0.28C TWIP steel was analyzed. The cold-rolled material, which showed a Brass-type texture at medium (30% and 50%), and additionally a γ-fiber at high (80%) deformation degrees, was subjected to isothermal annealing at 700°C. The influence of rolling degree/starting texture on the development of particular texture components was studied. After recrystallization a weakened, retained rolling texture was observed for the examined reduction levels. In addition to the deformation components, Brass and Goss, further α-fiber components were formed mainly by annealing twinning leading to the development of this fiber.
Publisher
Trans Tech Publications, Ltd.
Subject
Mechanical Engineering,Mechanics of Materials,Condensed Matter Physics,General Materials Science
Reference20 articles.
1. O. Bouaziz, S. Allain, C. P. Scott, P. Cugy and D. Barbier: Curr. Opin. Solid State Mater. Sci. Vol. 15 (2011), p.141.
2. B. C. De Cooman, O. Kwon and K. G. Chin: Mater. Sci. Technol. Vol. 28 (2012), p.513.
3. C. Haase, S. G. Chowdhury, L. A. Barrales-Mora, D. A. Molodov and G. Gottstein: Metall. Mater. Trans. A Vol. (2012), DOI: 10. 1007/s11661-012-1543-4.
4. Y. Lü, D. A. Molodov and G. Gottstein: ISIJ Int. Vol. 51 (5) (2011), p.812.
5. Y. Lü, B. Hutchinson, D. A. Molodov and G. Gottstein: Acta Mater. Vol. 58 (2010), p.3079.
Cited by
28 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献