Li X.M.,Zou Y.,Zhang Z.W.,Zou Z.D.,Du B.S.
Abstract
The intergranular corrosion of the weld metal of super Type 304H (UNS S30409) stainless steel during aging at 650°C was investigated using electrochemical potentiokinetic reactivation (EPR). Experimental results showed that the as-welded weld joint possesses a good corrosion-resistant property, but the formation of chromium-depleted zones caused by precipitation of Cr23C6 between cellular dendrites increased the reactivation ratio (Ra) when the weld metal was aged at 650°C for a prolonged time, indicating the acceleration of intergranular corrosion with increased aging time. Nevertheless, it was found that Cr23C6 showed the morphology with isolated particles after being aged for 500 h and Ra became stable.
Subject
General Materials Science,General Chemical Engineering,General Chemistry