Compound Development of Fe<sub>80</sub>Cr<sub>20</sub> Metallic Interconnect by Ball Milling and Ultrasonic Technique: Its Effect on Mass Gradation

Author:

Feriyanto Dafit, ,Zakaria Supaat,Pranoto Hadi,Romahadi Dedik,hidayat Imam, , , ,

Abstract

The investigation of metallic material for interconnect fuel cell application was very challenging due to interconnect operate at high temperature up to 1100<sup>0</sup>C. However, the main problem of metallic material is mass change at high temperature is inevitable. Therefore, this research aims to analyse the compound of Fe<sub>80</sub>Cr<sub>20</sub> and it effect of mass gradation. The methods were conducted by ultrasonic technique (UT) by frequency of 35 kHz, various ultrasonic time of 3, 3.5, 4, 4.5 and 5 h. Milling technique was conducted by milling time of 60 h with nitrogen gas condition. The analysis was conducted by Scanning Electron Microscope for compound investigation and Thermo Gravimetric Analyzer (TGA) for mass gradation analysis. The result shows that there are several compounds that developed after ball milling and ultrasonic technique such as Fe<sub>80</sub>Cr<sub>20</sub>, FeO<sub>2</sub> and Cr<sub>2</sub>O<sub>3</sub>. The UT samples shows the lowest mass gain of 31.917 mg is located at UT 4.5 h, while raw material has largest mass gain as compared to the other samples (treated samples). Meanwhile for milled and combination of milled and UT samples shows the lowest mass gain has observed at milled and UT 4.5 h with the value of 17.014 mg and 12.7 mg, respectively.

Publisher

Penerbit Universiti Kebangsaan Malaysia (UKM Press)

Subject

General Medicine

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3