Abstract
Abstract
In the study, the morphological properties of polyacrylonitrile (PAN) fibers produced by electrospinning at different needle diameters and solution flow rates were investigated. For this purpose, 20G and 22G diameter needles were used. The fibres were produced at flow rates of 0.5 ml/hr, 1 ml/hr and 1.5 ml/hr. Scanning electron microscopy (SEM) was used to measure nanofiber diameters. Statistical analyzes were made with the help of the SPSS program. It was observed that finer fibers were obtained as the needle diameter decreased. As the solution flow rate increased, thicker fibers were obtained. In addition, it was observed that the needle diameter and flow rate affect the fiber arrangement and interfiber spacing.
Subject
Industrial and Manufacturing Engineering,General Environmental Science,Materials Science (miscellaneous),Business and International Management
Reference47 articles.
1. Sabit, B. (2019). Elektro lif çekim (Electrospınnıng) yöntemiyle üretilen nanolif iplik özelliklerinin iyileştirilmesi (Yüksek Lisans Tezi). Tekirdağ Namık Kemal Üniversitesi, Tekirdağ.
2. Formhals, A. (1934). Process and apparatus for preparing artficial threads. US Patent, No.1, 975, 504.
3. Ramakrishna, S., Fujihara, K., Teo, W.E., Lim, T.C., Ma, Z. (2005). An ıntroduction to electrospinning and nanofibers. Singapore: World Scientific Publishing Co. Pte. Ltd.
4. Ghafari, E., Feng, Y., Liu, Y., Ferguson, I. and Lu, N. (2017). Investigating process-structure relations of ZnO nanofiber via electrospinning method. Composites Part B., 116, 40–45.
5. Liu, J., Chang, M. J. and Du, H. L. (2016). Facile preparation of cross-linked porous poly(vinyl alcohol) nanofibers by electrospinning. Mater. Lett., 183, 318–321.
Cited by
1 articles.
订阅此论文施引文献
订阅此论文施引文献，注册后可以免费订阅5篇论文的施引文献，订阅后可以查看论文全部施引文献