Influence of Heat Treatment on Magnetic Properties of Nanocrystalline Nd9Fe84Zr1B6 Ribbons Received by Rapid Solidification Method

Abstract

Influence of Heat Treatment on Magnetic Properties of Nanocrystalline Nd9Fe84Zr1B6Ribbons Received by Rapid Solidification MethodThe effect of the annealing on the phase composition and magnetic properties of nanocomposite melt-spun Nd9Fe84Zr1B6ribbons has been investigated. From the X-ray diffraction studies confirmed be thermomagnetic curves measurements results that the microstructure of the material investigated is composed of a mixture of magnetically hard Nd2Fe14B and soft α-Fe, Fe3B nanosized grains. The small amount of undesirable Nd2Fe23B3metastable phase has been found which do not decompose at the highest annealing temperature. The hysteresis loop measurements certify that the ribbon annealed at 863K show the best coupling between the hard and soft magnetic phases and thus the highest coercivity of 0.38T. The grain sizes increase with increasing annealing temperature causing the coercivity to be decrease.