Abstract
AbstractIn recent years, research on hyperdoped semiconductors has accelerated, displaying dopant concentrations far exceeding solubility limits to surpass the limitations of conventionally doped materials. Nitrogen defects in silicon have been extensively investigated for their unique characteristics compared to other pnictogen dopants. However, previous practical investigations have encountered challenges in achieving high nitrogen defect concentrations due to the low solubility and diffusivity of nitrogen in silicon, and the necessary non-equilibrium techniques, such as ion implantation, resulting in crystal damage and amorphisation. In this study, we present a single-step technique called high-pressure gas immersion excimer laser doping (HP-GIELD) to manufacture nitrogen-hyperdoped silicon. Our approach offers ultrafast processing, scalability, high control, and reproducibility. Employing HP-GIELD, we achieved nitrogen concentrations exceeding 6 at% (3.01 × 1021 at/cm3) in intrinsic silicon. Notably, nitrogen concentration remained above the liquid solubility limit to ~1 µm in depth. HP-GIELD’s high-pressure environment effectively suppressed physical surface damage and the generation of silicon dangling bonds, while the well-known effects of pulsed laser annealing (PLA) preserved crystallinity. Additionally, we conducted a theoretical analysis of light-matter interactions and thermal effects governing nitrogen diffusion during HP-GIELD, which provided insights into the doping mechanism. Leveraging excimer lasers, our method is well-suited for integration into high-volume semiconductor manufacturing, particularly front-end-of-line processes.
Funder
Nottingham Trent University
instituto nazionale di scienza e technologia quantistica
King Abdullah University of Science and Technology
Publisher
Springer Science and Business Media LLC
Reference50 articles.
1. Tong, Z., Bu, M., Zhang, Y., Yang, D. & Pi, X. Hyperdoped silicon: Processing, properties, and devices. J. Semicond. 43, 093101. https://doi.org/10.1088/1674-4926/43/9/093101 (2022).
2. Abe, T., Kikuchi, K., Shirai, S. & Murakoa, S. Impurities in silicon single crystals—A current view. In Semiconductor Silicon 1981: Proceedings of the Fourth International Symposium on Silicon Materials Science and Technology Vol. 815 (eds Huff, H. R. et al.) 54–71 (Springer, 1981).
3. Stein, H. J. Vibrational absorption bands for implanted nitrogen in crystalline silicon. Appl. Phys. Lett. 43, 296–298. https://doi.org/10.1063/1.94291 (1983).
4. Stein, H. J. Infrared absorption band for substitutional nitrogen in silicon. Appl. Phys. Lett. 47, 1339–1341. https://doi.org/10.1063/1.96273 (1985).
5. Jones, R., Öberg, S., Berg Rasmussen, F. & Bech Nielsen, B. Identification of the dominant nitrogen defect in silicon. Phys. Rev. Lett. 72, 1882–1885. https://doi.org/10.1103/PhysRevLett.72.1882 (1994).