Abstract
AbstractGradient nano-grained structures have been a promising technique to evade the strength-ductility trade-off in metals and alloys. Therefore, in this work, the effect of surface mechanical attrition treatment (SMAT) on the microstructure and corrosion behavior of the high-strength aluminum alloy was investigated. SMAT was performed at room temperature and liquid-nitrogen (LN2) flow conditions to generate two distinctly different initial gradient microstructures. Potentiodynamic polarization, electrochemical impedance spectroscopy, and intergranular corrosion tests were performed. Surface film characterization of untreated and treated samples was performed using X-ray photoelectron spectroscopy and time of flight secondary ion mass spectroscopy techniques. Result reveals significant microstructural changes in SMAT processed samples such as the formation of precipitates and dissolution of inherent phases. In addition, a reduced anodic dissolution rate was observed with the SMAT processed samples. Furthermore, the surface film characterization revealed a thicker oxide film with Cu and SiO2 enrichment in SMAT samples.
Funder
United States Department of Defense | United States Army | U.S. Army Research, Development and Engineering Command | Army Research Laboratory
Publisher
Springer Science and Business Media LLC
Subject
Materials Chemistry,Materials Science (miscellaneous),Chemistry (miscellaneous),Ceramics and Composites
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献