Microstructure Evolution and Molten Salt Corrosion Resistance Dependent on Pre-Oxidation Treatment of NiAl Coatings

Author:

Xu Shi-peng1,Zheng Yue-hong1,Zhan Fa-qi1,La Pei-qing1

Affiliation:

1. State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals, Lanzhou University of Technology, 730050, Lanzhou, China

Abstract

The chloride-infused molten salt shows the most potential as the medium for the upcoming generation of concentrated solar power system. However, the molten salt put for ward higher corrosion resistance demand on the critical components of concentrated solar power system. The application of NiAl coating proves to be a highly efficient method for preventing corrosion. In this paper, the microstructure, adhesion, and corrosion resistance of NiAl coatings on 310S stainless steel with/without pre-oxidation treatment were studied. The coating predominantly consisted of β-NiAl phase nanocrystals with an Al content of 41.0 at.%. Continuous α-Al2O3 oxide film was formed and no obvious cracks were observed after pre-oxidation. The adhesion strength of NiAl coating was increased by about 70% to 40.0 N through pre-oxidation. Importantly, the corrosion results of NiAl coatings by pre-oxidation treatment in the mixed salt of NaCl/MgCl2/KCl at 1073.15 K for 10 h showed no obvious diffusion of molten salt elements into the coatings. Compared to 310S stainless steel, the pre-oxidized coating sample exhibited a significant reduction of 50.2% in corrosion mass loss. The pre-oxidation of the NiAl coating creates an Al2O3 oxidation layer that effectively blocks corrosion, offering a new method for protecting stainless steels in concentrated solar power system plants.

Publisher

American Scientific Publishers

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3