Prasad K.,Kroll U.,Finger F.,Shah A.,Dorter J-L.,Howling A.,Baumann J.,Schubert M.
Abstract
ABSTRACTWe have investigated the influence of substrate temperature on the optoelectronic and structural properties of heavily doped μc-Si:H, prepared with the Very High Frequency Glow Discharge process. At substrate temperatures as low as 160°C we obtain, for films with 0.5μm thickness, maximum conductivities of 100 S/cm and 20 S/cm for <n> and <p> material, respectively. Starting from these values the deposition parameters were optimised for ultrathin layers having thicknesses in the range of 100 to 500Å. We observe that boron doping plays a critical role in the crystallisation of ultrathin films. The thinnest layers investigated so far show conductivities of 0.2 S/cm at d=100Å for <n>, and 0.2 S/cm at d=250Å for <p> material. These properties make μc-Si:H films attractive candidates to form tunnel junctions in tandem solar cells.
Publisher
Springer Science and Business Media LLC
Reference11 articles.
1. Preferential segregation of dopants in μc-Si:H
2. [8] Finger F. , Kroll U. , Viret V. , Shah A. , Beyer W. , Tang X. M. , Weber J. , Howling A. , Hollenstein Ch. , J. Appl. Phys. (1991) (submitted).
3. [7] Dorier J.L. , Diploma thesis, EPFL (1991).
4. Optical determination of mobility and carrier concentration in heavily doped polycrystalline silicon
Cited by
21 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献