Floating zone partial melting and solidification of SmBCO superconductor under low oxygen partial pressure

Abstract

Microstructure control of SmBCO superconductor was carried out using the floating zone partial melting and solidification method under 0.01 atm oxygen partial pressure which is a preferable atmosphere to obtain a crystal with stoichiometric SmBCO. The growth rate, initial composition, and addition of small amount of platinum dependences on the microstructure formations of the (Sm211 + L) mixture during melting and the Sm123 or Sm123/211 during solidification were investigated. Furthermore, superconductive properties of the solidified Sm123/211 were measured by SQUID after appropriate oxygen annealing. Estimated critical current density of the single crystalline Sm123/211 was 3.6 × 104 A/cm at 77 K, 1 T.