Influence of CaCO3 on Density and Compressive Strength of Calcium Aluminate Cement-Based Cementitious Materials in Binder Jetting

Abstract

We investigated the impact of CaCO3 addition on the density and compressive strength of calcium aluminate cement (CAC)-based cementitious materials in binder jetting additive manufacturing (BJAM). To confirm the formation of a uniform powder bed, we examined the powder flowability and powder bed density for CaCO3 contents ranging from 0 to 20 wt.%. Specifically, powders with avalanche angles between 40.1–45.6° formed a uniform powder bed density with a standard deviation within 1%. Thus, a 3D printing specimen (green body) fabricated via BJAM exhibited dimensional accuracy of less than 1% across the entire plane. Additionally, we measured the hydration characteristics of CAC and the changes in compressive strength over 30 days with the addition of CaCO3. The results indicate that the addition of CaCO3 to CAC-based cementitious materials forms multimodal powders that enhance the density of both the powder bed and the green body. Furthermore, CaCO3 promotes the formation of highly crystalline monocarbonate (C4AcH11) and stable hydrate (C3AH6), effectively inhibiting the conversion of CAC and showing compressive strengths of up to 5.2 MPa. These findings suggest a strong potential for expanding the use of BJAM across various applications, including complex casting molds, cores, catalyst supports, and functional architectural interiors.