Abstract
Based on previous work, where Al-Si-Cu-Ni alloy was successfully manufactured by laser powder bed fusion (PBF-LB/M) technology, in this study, we further observe the microstructure of the alloy, analyze the formation mechanism of the microstructure during solidification, and discuss their implications for the mechanical properties. The results indicate that the microstructure comprises multi-level cellular heterogeneous structures, with an α-Al matrix in the interior of the cellular structure and Cu- and Ni-rich phases clustered at the boundaries, intertwined with the silicon network. During solidification, α-Al solidifies first and occupies the core of the cells, while Si phases and Cu- and Ni-rich phases deposit along the cellular boundaries under the influence of surface tension. During the solidification process of cellular boundaries, influenced by spinodal decomposition and lattice spacing, Si phases and Cu- and Ni-rich phases interconnect and distribute crosswise, collectively forming multi-level cellular structures. The refined cellular microstructure of the PBF-LB/M Al-Si-Cu-Ni alloy enhances the mechanical properties of the alloy. The alloy exhibits a bending strength of 766 ± 30 MPa, a tensile strength and yield strength of 437 ± 6 MPa and 344 ± 4 MPa, respectively, with a relatively low fracture elongation of approximately 1.51 ± 0.07%. Subsequent improvement can be achieved through appropriate heat treatment processes.