Through surface nanocrystallization and low-temperature ion sulfurization, the nanocrystalline/FeS thin film with excellent friction-reduction and antiwear properties was fabricated on the surface of AISI321 stainless steel. The nanocrystallization treatment formed the high hardness and active nanocrystalline structure on the surface of AISI321, with the harness increased from 4.6 GPa to 7.56 GPa. Furthermore, the significantly refined nanostructure strongly increased the concentration of S element in comparison with the single-sulfurized layer on the substrate. Tribological tests reveal that both the original AISI321 substrate and the single-sulfurizing-treated samples are subject to severe abrasion. Single nanocrystallization treatment can improve the wear resistance of AISI321, while the compound treatment can obviously improve the comprehensive tribological properties. The compound-modified layer presents excellent tribological properties with the lowest coefficient of friction (COF) of 0.33, which is related to the increased hardness of the substrate and increased thickness, density, and homogeneity of the sulfurized layer. Furthermore, a physical model is developed for the vacuum tribological behavior of the samples after different treatments. This model provides a reference for revealing the tribological mechanism of the compound-modified layer treated using surface nanocrystallization-assisted chemical heat treatment.
Subject
General Materials Science
Reference22 articles.
1. Study of Magnetic Abrasive Finishing for AISI321 Stainless Steel;Saraeian;Mater. Manuf. Process.,2016
2. Effect of ultrasonic vibrations in TIG welded AISI321 stainless steel: Microstructure and mechanical properties;Mehran;Mater. Res. Express.,2018
3. Structure and friction-reducing property of low temperature ion sulphuration layer;Zhang;Chin. J. Mater. Res.,2000
4. Surface texturing for adaptive Ag/MoS2 solid lubricant plating;Huang;Rare Met.,2012
5. Tribological properties of laser cladding TiB2 particles reinforced Ni-base alloy composite coatings on aluminum alloy;He;Rare Met.,2015
Cited by
2 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献