Author:
Gao Peihu,Chen Baiyang,Zeng Shencong,Yang Zhong,Guo Yongchun,Liang Minxian,Xu Tao,Li Jianping
Abstract
Plasma-sprayed nickel-based self-fusion alloy coatings were annealed in a vacuum at 990, 1020 and 1050 °C for 20 min to increase the bonding between the compacted graphite cast iron substrate and coating, as well as the inner cohesion of the coatings. It was found that nickel and chromium diffused between nickel-based alloy coatings and compacted graphite cast iron substrate. A metallurgical translation zone with a thickness up to 1145 μm formed during the vacuum annealing, which resulted in an enhancement of the adhesion between the coating and substrate. The adhesion strength at room temperature was increased from the as-sprayed coating of 33.4 MPa to the annealed one of 163 MPa. Meanwhile, the adhesion strength at 500 °C reached 146 MPa. Conversely, the inner cohesion of the coating was improved with the particles’ interfaces healed after vacuum annealing. The micro-hardness of the annealed coatings was increased to 902 HV from the as-sprayed one of 578 HV.
Funder
National Natural Science Foundation of China
Shaanxi Key Science and Technology Innovation Team Project
Subject
General Materials Science,Metals and Alloys
Cited by
7 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献