Influence of Isothermal Annealing in the 600 to 750 °C Range on the Degradation of SAF 2205 Duplex Stainless Steel

Author:

Burja Jaka12ORCID,Žužek Borut1,Šetina Batič Barbara1ORCID

Affiliation:

1. Institute of Metals and Technology, 1000 Ljubljana, Slovenia

2. Department for Materials and Metallurgy, Faculty of Natural Sciences and Engineering, University of Ljubljana, 1000 Ljubljana, Slovenia

Abstract

We studied the effect of isothermal annealing (600–750 °C, 1 to 1000 min) on the microstructure and mechanical properties of SAF 2205 duplex stainless steel. Impact toughness was found to be significantly more affected than hardness by annealing. Annealing at 750 °C for 1000 min resulted in a more than 90% decrease in impact toughness, while hardness only increased by 25%. Tensile strength increased up to 100 MPa, but elongation decreased by more than 50% under the same conditions. Sigma phase formation was minimal at lower temperatures (650 °C and below) but increased significantly at higher temperatures. At 750 °C and 1000 min of annealing, the ferrite content dropped from 50% to 16%. These findings suggest that annealing temperature and time need to be carefully controlled to avoid a reduction in impact toughness and ductility caused by sigma phase precipitation. The harmful effect of sigma phase precipitation on mechanical properties was directly shown.

Funder

Slovenian Research Agency

Publisher

MDPI AG

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3