Influence of the Composition of Provisional Luting Materials on the Bond Strength of Temporary Single-Tooth Crowns on Titanium Abutments

Abstract

In addition to zinc oxide-based cements, resin-based materials are also available for temporary cementation. The aim of this in vitro study was to determine the influence of the different material compositions on temporary bonds. In nine test series (n = 30), temporary bis-acrylate single-tooth crowns were bonded onto prefabricated titanium abutments with nine different temporary luting materials. After simulating an initial (24 h, distilled water, 37 °C), a short-term (7 days, distilled water, 37 °C) and a long-term provisional restoration period (12h, distilled water, 37 °C; thermocycling: 5000 cycles) in subgroups (n = 10), the bond strength was examined using a combined tensile–shear test. Statistical analysis was performed by univariate analysis of variance or a non-parametric Kruskal–Wallis test, followed by post hoc tests. Of the three resin-based materials, two showed significantly higher bond strength values compared to all other materials (p < 0.001), regardless of the storage procedure. The resin-based materials were followed by eugenol-free and eugenol-containing zinc oxide materials. Significant intragroup differences were observed between the composite-based materials after all storage periods. This was only observed for some of the zinc oxide-based materials. The results show that under in vitro conditions, not only the composition of the temporary luting materials but also the different storage conditions have a significant influence on temporary bonds.