Relation between Ga Vacancies, Photoluminescence, and Growth Conditions of MOVPE-Prepared GaN Layers

Abstract

A set of GaN layers prepared by metalorganic vapor phase epitaxy under different technological conditions (growth temperature carrier gas type and Ga precursor) were investigated using variable energy positron annihilation spectroscopy (VEPAS) to find a link between technological conditions, GaN layer properties, and the concentration of gallium vacancies (VGa). Different correlations between technological parameters and VGa concentration were observed for layers grown from triethyl gallium (TEGa) and trimethyl gallium (TMGa) precursors. In case of TEGa, the formation of VGa was significantly influenced by the type of reactor atmosphere (N2 or H2), while no similar behaviour was observed for growth from TMGa. VGa formation was suppressed with increasing temperature for growth from TEGa. On the contrary, enhancement of VGa concentration was observed for growth from TMGa, with cluster formation for the highest temperature of 1100 °C. From the correlation of photoluminescence results with VGa concentration determined by VEPAS, it can be concluded that yellow band luminescence in GaN is likely not connected with VGa; additionally, increased VGa concentration enhances excitonic luminescence. The probable explanation is that VGa prevent the formation of some other highly efficient nonradiative defects. Possible types of such defects are suggested.