Rheological Properties and Microstructural Analysis of Asphalt Binder Doped with Anti-Stripping Agent after Aging

Author:

Liu Keyan,Xu Yongli,Gao Dapeng,Yang Songhan

Abstract

In order to comprehensively explore the long-term durability of asphalt mixed with an anti-stripping agent, laboratory tests were carried out on base asphalt, SBS modified asphalt and base asphalt mixed with an anti-stripping agent after long-term aging. The rheological properties, chemical composition and microscopic morphology of the three asphalts before and after aging were compared and analyzed from macroscopic and microscopic angles. The results show that the modulus of asphalt is more affected by temperature than aging, and the anti-aging ability of the asphalt with the anti-stripping agent is better than that of base asphalt and slightly worse than that of SBS modified asphalt. The change in the absorption peak intensity before and after the aging of asphalt with the anti-stripping agent is the same as those of the base asphalt and SBS modified asphalt at 2920 cm−1 and 2850 cm−1, while the opposite pattern is observed in other four places. The honeycomb structures of the base asphalt and SBS modified asphalt became longer and the number of peaks increased slightly after aging. However, the asphalt surface with the anti-stripping agent had no obvious honeycomb structures before aging, and there were obvious honeycomb structures after aging, the number of which was between those of the base asphalt and SBS modified asphalt after aging; moreover, the lengths of honeycomb structures were still significantly smaller than those of the base asphalt after aging. This study investigated the performance changes of the anti-stripping-agent asphalt before and after long-term aging at multiple scales and compared the asphalt mixed with the anti-stripping agent with base asphalt and SBS modified asphalt to fully evaluate its long-term durability.

Publisher

MDPI AG

Subject

Materials Chemistry,Surfaces, Coatings and Films,Surfaces and Interfaces

Reference40 articles.

1. Zhou, B. (2018). Test Method and Evaluation of Anti—Stripping Ability of Porous Asphalt Mixture. [Master’s Thesis, Harbin Institute of Technology].

2. Zhang, M. (2019). Influence Mechanism of Aging and Water Damage on Spalling Resistance of Asphalt Drainage Pavement. [Ph.D. Thesis, Southeast University].

3. Zhang, G.H., Qiu, J.H., Zhao, J.Z., Wei, D.B., and Wang, H. (2020). Development of Interfacial Adhesive Property by Novel Anti-Stripping Composite between Acidic Aggregate and Asphalt. Polymers, 12.

4. Research progress of asphalt anti-stripping agents;Peng;Mater. Rep.,2014

5. Comprehensive analysis of surface free energy of asphalts and aggregates and the effects of changes in pH;Howson;Constr. Build. Mater.,2011

Cited by 2 articles. 订阅此论文施引文献 订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献

同舟云学术

1.学者识别学者识别

2.学术分析学术分析

3.人才评估人才评估

"同舟云学术"是以全球学者为主线,采集、加工和组织学术论文而形成的新型学术文献查询和分析系统,可以对全球学者进行文献检索和人才价值评估。用户可以通过关注某些学科领域的顶尖人物而持续追踪该领域的学科进展和研究前沿。经过近期的数据扩容,当前同舟云学术共收录了国内外主流学术期刊6万余种,收集的期刊论文及会议论文总量共计约1.5亿篇,并以每天添加12000余篇中外论文的速度递增。我们也可以为用户提供个性化、定制化的学者数据。欢迎来电咨询!咨询电话:010-8811{复制后删除}0370

www.globalauthorid.com

TOP

Copyright © 2019-2024 北京同舟云网络信息技术有限公司
京公网安备11010802033243号  京ICP备18003416号-3