Abstract
The time-dependence of electrochemical reduction current, which was observed during the one-dimensional (1-D) crystal growth of ferromagnetic cobalt nanowire arrays, was analyzed by Johnson–Mehl–Avrami–Kolmogorov (JMAK) theory. Textured hcp-Co nanowire arrays were synthesized by potentio-static electrochemical reduction of Co2+ ions in anodized aluminum oxide (AAO) nanochannel films. Crystal growth geometry factor n in the JMAK equation was determined to be ca. 1. Hence, the electrochemical crystal growth process of a numerical nanowires array can be explained by 1-D geometry. The crystal nucleation frequency factor, k in JMAK equation was estimated to be the range between 10−4 and 10−3. Our experimental results revealed that the crystal nucleation site density Nd increased up to 2.7 × 10−8 nm−3 when increasing the overpotential for cobalt electrodeposition by shifting the cathode potential down to −0.85 V vs. Ag/AgCl. The (002) crystal orientation of hcp-Co nanowire arrays was, remarkably, observed by decreasing Nd. Spontaneous magnetization behavior was observed in the axial direction of nanowires. By decreasing the overpotential for cobalt electrodeposition, the coercivity of the nanocomposite film increased and reached up to 1.88 kOe, with a squareness of ca. 0.9 at room temperature.
Funder
Japan Society for the Promotion of Science
Japan Science and Technology Agency
Iketani Science and Technology Foundation
Subject
Inorganic Chemistry,Condensed Matter Physics,General Materials Science,General Chemical Engineering
Cited by
11 articles.
订阅此论文施引文献
订阅此论文施引文献,注册后可以免费订阅5篇论文的施引文献,订阅后可以查看论文全部施引文献